PEEK · 30% 탄소섬유

Joyrun K10CA30

Matches Victrex® 450CA30

30% carbon-fibre reinforced PEEK. The highest stiffness and strength in the family (265 MPa tensile) combined with low thermal expansion, optimised for metal-replacement structural parts and high-load components. Equivalent to the Victrex® 450CA30.

265 MPa TensileHDT 336°CMetal ReplacementLow Thermal Expansion≙ Victrex® 450CA30
TECHNICAL DOCUMENTS

Download the official documents for Joyrun K10CA30.

Stocked in Korea (standing inventory) · Evaluation samples available · engineering reply within 24 hours

Supply information

Stock and lead time confirmed at the time of enquiry

Joyrun K10CA30 is a PEEK · 30% 탄소섬유 grade supplied in Korea by Octud Co., Ltd. Stocked in Korea (standing inventory); minimum order 25 kg; evaluation samples available. Drop-in candidate for parts currently moulded in Victrex® 450CA30.

Korean stock
Stocked in Korea (standing inventory)
Lead time
Ex-stock: 1–2 days nationwide · indent lead time on request
Minimum order (MOQ)
25 kg
Equivalency review
Victrex® 450CA30

Typical property data

Tested at 23°C / 50% RH, dry as moulded. Source: Joyrun Joyrun K10CA30 TDS.

Mechanical PropertiesMechanical Properties
PROPERTYMETHODUNITVALUE
Tensile StrengthISO 527MPa265
Tensile Strength
ISO 527 · MPa
265
Tensile ModulusISO 527GPa23
Tensile Modulus
ISO 527 · GPa
23
Elongation at BreakISO 527%1.7
Elongation at Break
ISO 527 · %
1.7
Flexural StrengthISO 178MPa370
Flexural Strength
ISO 178 · MPa
370
Flexural ModulusISO 178GPa23
Flexural Modulus
ISO 178 · GPa
23
Charpy, unnotchedISO 179/1UkJ/m²45
Charpy, unnotched
ISO 179/1U · kJ/m²
45
Izod, notchedISO 180/AkJ/m²9.0
Izod, notched
ISO 180/A · kJ/m²
9.0
Thermal PropertiesThermal Properties
PROPERTYMETHODUNITVALUE
Melting PointISO 11357°C343
Melting Point
ISO 11357 · °C
343
Glass Transition TempISO 11357°C143
Glass Transition Temp
ISO 11357 · °C
143
Heat Deflection Temperature HDT (1.8 MPa)ISO 75A-f°C336
Heat Deflection Temperature HDT (1.8 MPa)
ISO 75A-f · °C
336
Coeff. of Thermal ExpansionASTM D696ppm·K⁻¹10
Coeff. of Thermal Expansion
ASTM D696 · ppm·K⁻¹
10
Thermal ConductivityISO/CD 22007-4W/(m·K)0.95
Thermal Conductivity
ISO/CD 22007-4 · W/(m·K)
0.95
Electrical PerformanceElectrical Performance
PROPERTYMETHODUNITVALUE
Dielectric Strength, 2 mmIEC 60243-1kV/mm—
Dielectric Strength, 2 mm
IEC 60243-1 · kV/mm
—
PermittivityIEC 62631——
Permittivity
IEC 62631 · —
—
Volume ResistivityIEC 62631Ω·cm10⁵
Volume Resistivity
IEC 62631 · Ω·cm
10⁵
Other PropertiesOther Properties
PROPERTYMETHODUNITVALUE
Color——Black
Color
— · —
Black
Melt Flow Index MFI (380°C, 5 kg)ISO 1133g/10min2–4
Melt Flow Index MFI (380°C, 5 kg)
ISO 1133 · g/10min
2–4
DensityISO 1183g/cm³1.40 ± 0.02
Density
ISO 1183 · g/cm³
1.40 ± 0.02
Water Absorption (23°C, 24h)ISO 62-1%0.04
Water Absorption (23°C, 24h)
ISO 62-1 · %
0.04
Moulding Shrinkage, parallel—%0.1
Moulding Shrinkage, parallel
— · %
0.1
Moulding Shrinkage, vertical—%0.5
Moulding Shrinkage, vertical
— · %
0.5
Shore HardnessISO 868—88
Shore Hardness
ISO 868 · —
88
Flammability RatingUL 94classV-0
Flammability Rating
UL 94 · class
V-0
Coefficient of FrictionASTM D3702—0.15–0.25
Coefficient of Friction
ASTM D3702 · —
0.15–0.25

※ Values are typical, not specification limits. Verify against the current TDS during design validation.