PSU · Polysulfone

Ultrason® S 3010 MR

Name: Ultrason® S 3010 MR
Brand: Ultrason®
Availability: InStock

이형성을 최적화한 고점도 폴리설폰(PSU) 사출 그레이드. S 3010의 인성과 내화학성을 유지하면서 탈형 저항을 낮춰, 복잡한 형상이나 깊은 리브가 있는 부품의 이형 불량과 사이클 타임을 줄입니다.

이형성 최적화 (Mould Release)고점도 · 고인성내화학성 개선HDT/A 176°C

Request a quote →Request sample

TECHNICAL DOCUMENTS

Download the official documents for Ultrason® S 3010 MR.

Technical Data Sheet (TDS)PDF · English · BASF original Safety Data Sheet (SDS)PDF · GHS format Processing Data SheetPDF · drying, barrel temperature, mould conditions · BASF 02/2026

Held in Korean stock · engineering reply within 24 hours

Typical property data

Tested at 23°C / 50% RH, dry as moulded. Source: BASF Ultrason® S 3010 MR TDS.

General PropertiesGeneral Properties

PROPERTYMETHODUNITVALUE

DensityISO 1183g/cm³1.23

Density

ISO 1183 · g/cm³

1.23

Viscosity NumberISO 307cm³/g72

Viscosity Number

ISO 307 · cm³/g

Melt Volume Flow Rate MVR (360°C/10 kg)ISO 1133cm³/10 min52

Melt Volume Flow Rate MVR (360°C/10 kg)

ISO 1133 · cm³/10 min

Water Absorption (수중 포화, 23°C)ISO 62%0.8

Water Absorption (수중 포화, 23°C)

ISO 62 · %

0.8

(23°C/50% r.h.)ISO 62%0.3

(23°C/50% r.h.)

ISO 62 · %

0.3

Moulding Shrinkage (평행 방향)ISO 294-4%0.70

Moulding Shrinkage (평행 방향)

ISO 294-4 · %

0.70

Moulding Shrinkage (직각 방향)ISO 294-4%0.73

Moulding Shrinkage (직각 방향)

ISO 294-4 · %

0.73

Mechanical PropertiesMechanical Properties

PROPERTYMETHODUNITVALUE

Tensile ModulusISO 527-1/-2MPa2,600

Tensile Modulus

ISO 527-1/-2 · MPa

2,600

Stress at Yield, 50 mm/minISO 527-1/-2MPa75

Stress at Yield, 50 mm/min

ISO 527-1/-2 · MPa

Strain at YieldISO 527-1/-2%5.5

Strain at Yield

ISO 527-1/-2 · %

5.5

Charpy Notched Impact Strength (23°C)ISO 179/1eAkJ/m²5.5

Charpy Notched Impact Strength (23°C)

ISO 179/1eA · kJ/m²

5.5

Charpy Notched Impact Strength (−30°C)ISO 179/1eAkJ/m²6

Charpy Notched Impact Strength (−30°C)

ISO 179/1eA · kJ/m²

Charpy Unnotched Impact Strength (23°C)ISO 179/1eUkJ/m²Non-break

Charpy Unnotched Impact Strength (23°C)

ISO 179/1eU · kJ/m²

Non-break

Ball Indentation Hardness (358 N/30 s)ISO 2039-1MPa135

Ball Indentation Hardness (358 N/30 s)

ISO 2039-1 · MPa

135

Thermal PropertiesThermal Properties

PROPERTYMETHODUNITVALUE

DSC, 10°C/minISO 11357-1/-2°C187

DSC, 10°C/min

ISO 11357-1/-2 · °C

187

Heat Deflection Temperature HDT/A (1.8 MPa)ISO 75-1/-2°C176

Heat Deflection Temperature HDT/A (1.8 MPa)

ISO 75-1/-2 · °C

176

Coefficient of Linear Thermal Expansion CLTE (23–80°C, 평행)ISO 11359-1/-2E-6/K53

Coefficient of Linear Thermal Expansion CLTE (23–80°C, 평행)

ISO 11359-1/-2 · E-6/K

Coefficient of Linear Thermal Expansion CLTE (140°C, 평행)DIN 53752E-6/K60

Coefficient of Linear Thermal Expansion CLTE (140°C, 평행)

DIN 53752 · E-6/K

Flammability Rating (1.5 mm)UL 94classHB

Flammability Rating (1.5 mm)

UL 94 · class

Flammability Rating (3 mm)UL 94classV-2

Flammability Rating (3 mm)

UL 94 · class

V-2

ProcessingProcessing

PROPERTYMETHODUNITVALUE

가공 방식——사출 (M)

가공 방식

— · —

사출 (M)

Melt Temperature—°C330 – 390

Melt Temperature

— · °C

330 – 390

Mould Temperature—°C120 – 160

Mould Temperature

— · °C

120 – 160

(가공 전)——130–150°C, 4 h 이상

(가공 전)

— · —

130–150°C, 4 h 이상

※ Values are typical, not specification limits. Verify against the current TDS during design validation.

Ultrason® S 3010 MR

Typical property data